Aluminium tube extrusion for straining beam of luggage

Name: Aluminium tube extrusion for straining beam of luggage
Brand: Customized
SKU: 8207721
Rating: 5.0 (94 reviews)

High quality customized aluminum profile for straining beam of luggage with assembly , material: AL6063-T5, finish: anodizing, Manufacture technology:extrusion and cnc machining...

Material:	AL6063-T5
Finish:	Anodizing
Availability:

Quantity:



Inquire Add to Basket

Model:
Customized
Brand:
Customized
Code:
SHHEATSINK015

joining aluminium extrusions

Material	AL6063-T5
Surface finish	Anodized
Manufacture technology	Extrusion and CNC milling
Application	Automotive, Automation, Test systems, Sensors, Medical, Sports, Consumer, Home appliance,Electronic, Pumps, Computers, Power and energy, Architecture, Printing, Food, Textile machinery, Optical, Lighting, Security and safety, AOI, SMT equipment, etc.
Main Export Markets	North America, Europe, Mid East, Asia, Australia, Central/South America, etc.
Packing	Standard export package, Carton, Wood pallet or as requirement
Inspection	In-house or third party, all the products are strictly inspected by skilled QC
Service Type	OEM & ODM

standard aluminium profiles custom aluminium profiles powder coated aluminium profiles aluminium extrusions for led lighting

Get A Free Quote

Products

About Us

Contact Us

(+86)-0769-88050188
sales@shunhogroup.com.hk
Room 806, Block A, worldecono
mic and trade center No. 11 Dong
guan Avenue, Dongcheng District ,
Dongguan, China

Message

Friendship links：PCB supplier ; Strut mounts; Photograph & design; PCBA assembly in China

Alloy	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Impurity	Al
6063	0.2-0.6	0.35	0.1	0.1	0.45-0.9	0.1	0.1	0.1	0.15	Rest
6061	0.4-0.8	0.7	0.15-0.4	0.15	0.8-1.2	0.04-0.35	0.25	0.15	0.15	Rest
6060	0.3-0.6	0.1-0.3	0.1	0.1	0.35-0.6	-	0.15	0.1	0.15	Rest
6005	0.6-0.9	0.35	0.1	0.1	0.40-0.6	0.1	0.1	0.1	0.15	Rest

Alloy	Temper	Tensile strength	Yield strength	Elongation
6063	T5	≥ 160Mpa	≥ 110Mpa	≥ 8%
6063	T6	≥ 205Mpa	≥ 180Mpa	≥ 8%
6061	T6	≥ 265Mpa	≥ 245Mpa	≥ 8%

Alloy	Si	Fe	Cu	Mn	Mg	Cr	Zn	Ti	Impurity	Al
6063	0.2-0.6	0.35	0.1	0.1	0.45-0.9	0.1	0.1	0.1	0.15	Rest
6061	0.4-0.8	0.7	0.15-0.4	0.15	0.8-1.2	0.04-0.35	0.25	0.15	0.15	Rest
6060	0.3-0.6	0.1-0.3	0.1	0.1	0.35-0.6	-	0.15	0.1	0.15	Rest
6005	0.6-0.9	0.35	0.1	0.1	0.40-0.6	0.1	0.1	0.1	0.15	Rest

Alloy	Temper	Tensile strength	Yield strength	Elongation
6063	T5	≥ 160Mpa	≥ 110Mpa	≥ 8%
6063	T6	≥ 205Mpa	≥ 180Mpa	≥ 8%
6061	T6	≥ 265Mpa	≥ 245Mpa	≥ 8%